鉻礦砂 是一種天然存在的尖晶石，主要由鉻和鐵的氧化物組成。它是鉻鐵生產的副產品，主要用於鑄造應用和玻璃生產。
鑄造鉻鐵礦砂技術數據表：
| 化學成分 | |
| 三氧化二鉻 | ≥46.0% |
| 二氧化矽 | ≤1.0% |
| 氧化亞鐵 | ≤26.5% |
| 高的 | ≤0.3% |
| 氧化鎂 | ≤10% |
| 三氧化二鋁 | ≤15.5% |
| 磷 | ≤0.003% |
| S | ≤0.003% |
| 鉻/鐵 | 1.55:1 |
| 典型物理特性 | |
| 硬度： | 莫氏：5.5-6 |
| 熔點： | 2180℃昇華 |
| 燒結點： | >1800℃ |
| 燒結的 | 1600℃ |
| 比重： | 4.0-4.8克/立方厘米 |
| 堆積密度（LPD）： | 2.5-3 g/cm3 |
| Color: | Black |
| PH | 7-9 |
| Percentage of free acid present in the sand | 0% |
| The amount of the acid | ≤2ML |
| Percentage of soil | ≤0.1 |
| Percentage of Moisture | ≤0.1 |
|
Available size: AFS25-30,AFS25-35, AFS30-35,AFS35-40,AFS40-45,AFS45-50,AFS40-50,AFS50-55,AFS55-60,AFS60-65 325# 400# |
|
THE ADVANTAGE OF FOUNDRY CHROMITE SAND
Comparing with silica sand,chromite sand can avoid most sand stick on the casting,therefor it can also save cost to make surface treatment. Moreover,chromite can be recycle used for several times upon to different technology.
Over all the chromite ore in the world, the one from South Africa are of the best quality level.Sicheng Abrasive import original chromite ore from there and refine it to better purity to 46% Cr2O3.
MAIN APPLICATIONS OF FOUNDRY CHROMITE SAND
鑄造行業中的鉻鐵礦砂
其特性使該材料可在高強度灰鐵和鋼鑄造廠中用作型 芯和模具
製沙。其高導熱性使其具有良好的冷卻性能，低熱膨脹性使其具有良好的尺寸穩定性。其鹼度接近中性，允許使用多種樹脂
粘結系統和無機粘結劑，具有高耐火度和寬篩分分佈。
鋼鐵工業中的鉻鐵礦砂
在鋼鐵生產中，鉻鐵礦砂也用作填料，用於保護大型鋼包中的滑動水口。
玻璃工業中的鉻鐵礦砂
當磨成細粉時，鉻鐵礦砂可用於生產綠色玻璃飲料容器。
如何選擇粒度？
一般情況下，需要製造的鑄件越小，鑄造廠採用的粒度越細，如下圖所示，供參考：
|
小於500KGS |
500-1000公斤 |
1-10噸 |
10-30噸 |
30-100噸 |
|
AFS40-70 |
AFS 45-50 |
AFS 45-50 |
AFS40-45 |
AFS 35-40 |
鑄造鉻鐵礦砂包